Lactide is one of the most popular and promising monomers for the synthesis of biocompatible and biodegradable polylactide and its copolymers. The goal of this work was to carry out a full cycle of polylactide production from lactic acid. Process conditions and ratios of reagents were optimized, and the key properties of the synthesized polymers were investigated. The influence of synthesis conditions and the molecular weight of lactic acid oligomers on the yield of lactide was studied. Lactide polymerization was first carried out in a 500 mL flask and then scaled up and carried out in a 2000 mL laboratory reactor setup with a combined extruder. Initially, the lactic acid solution was concentrated to remove free water; then, the oligomerization and synthesis of lactide were carried out in one flask in the presence of various concentrations of tin octoate catalyst at temperatures from 150 to 210 °C. The yield of lactide was 67–69%. The resulting raw lactide was purified by recrystallization in solvents. The yield of lactide after recrystallization in butyl acetate (selected as the optimal solvent for laboratory purification) was 41.4%. Further, the polymerization of lactide was carried out in a reactor unit at a tin octoate catalyst concentration of 500 ppm. Conversion was 95%; Mw = 228 kDa; and PDI = 1.94. The resulting products were studied by differential scanning calorimetry, NMR spectroscopy and gel permeation chromatography. The resulting polylactide in the form of pellets was obtained using an extruder and a pelletizer.