This study prepares composite panels with three Polylactic acid (PLA)-based materials via the multi-material fused filament fabrication method. The influences of four processing parameters on the mechanical properties of 3D-printed samples are investigated employing the Taguchi method. These parameters include the relative volume ratio, material printing order, filling pattern, and filling density. A “larger is better” signal-to-noise analysis is performed to identify the optimal combination of printing parameters that yield maximum bending strength and bending modulus of elasticity. The results reveal that the optimal combination of printing parameters that maximizes the bending strength involves a volume ratio of 1:1:2, a material sequence of PLA/foam-agent-modified eco-friendly PLA (ePLA-LW)/glass fiber-reinforced eco-friendly PLA (ePLA-GF), a Gyroid filling pattern, and a filling density of 80%, and the optimal combination of printing parameters for maximum bending modulus involves a volume ratio of 1:2:1 with a material sequence of PLA/ePLA-LW/ePLA-GF, a Grid filling pattern, and 80% filling density. The Taguchi prediction method is utilized to determine an optimal combination of processing parameters for achieving optimal flexural performances, and predicted outcomes are validated through related experiments. The experimental values of strength and modulus are 43.91 MPa and 1.23 GPa, respectively, both very close to the predicted values of 46.87 MPa and 1.2 GPa for strength and modulus. The Taguchi experiments indicate that the material sequence is the most crucial factor influencing the flexural strength of the composite panels. The experiment result demonstrates that the flexural strength and modulus of the first material sequence are 67.72 MPa and 1.53 GPa, while the flexural strength and modulus of the third material sequence are reduced to 27.09 MPa and 0.72 GPa, respectively, only 42% and 47% of the first material sequence. The above findings provide an important reference for improving the performance of multi-material 3D-printed products.