Recent progress has seen multiple Ta2O5 polymorphs generated by different synthesis techniques. However, discrepancies arise when these polymorphs are produced in widely varying thermodynamic conditions and characterized using different techniques. This work aimed to characterize and compare Ta2O5 particles formed at high and low temperatures using nanosecond pulsed laser ablation (PLA) and continuous wave (CW) laser heating of a local area of tantalum in either air or an 18O2 atmosphere. Scanning electron microscopy (SEM) and Raman spectroscopy of the micrometer-sized particles generated by PLA were consistent with either a localized amorphous Ta2O5 phase or a similar, but not identical, crystalline β-Ta2O5 phase. The Raman spectrum of the material formed at the point of CW laser impingement was in good agreement with the previously established ceramic “H-Ta2O5” phase. TEM and electron diffraction analysis of these particles indicated the phase structure matched an oxygen-vacated superstructure of monoclinic H-Ta2O5. Further from the point of laser impingement, CW heating produced particles with a Raman spectrum that matched β-Ta2O5. We confirmed that the high-temperature ceramic phase characterized in previous work by Raman spectroscopy was the same monoclinic phase characterized in different work by TEM and could be produced by direct laser heating of metal in air.